Low Smoke and Halogen-freeSelf-bonding Fire-resistance Tape

Code: XF-FHD-108

Color: White

XF-FHD-108 It is a white low-smoke halogen-free self-adhesive fireproof belt, made of special PlB material, with excellent flame retardant performance. lt is wound on the appearance of power and communication cables in various construction environments, and can rapidly expand when in contact with the flame to form an oxygen-resistant and fire-resistant carbonized layer, timely and effectively preventing the ignition and flame extension of cables.

• Soft, elastic, good shape-dependent, easy to evenly cover accessories of various shapes;

• Self-adhesive, good self-melting, easy installation, no need to fix other materials;
• Lightweight, thin thickness, easy for cable heat dissipation;

• Excellent flame retardant performance, flame retardant gradeup to UL94 v-0；

• Good ultraviolet resistance, ozone resistance, resistance to water, oil, salt, acid, alkali, and other chemical reagents;

• Halogen-free, extremely low toxicity and corrosion during事combustion, low smoke density, especially suitable for indoor. tunnel and subway use.

CONTACT NOW PDF DOWNLOAD

Details

Tags

PRODUCT APPLICATION

• Used for cable fire prevention, to strengthen the fireproof performance of cable sheath;

• Suitable for additional insulation and cable parts prone to failure where there are fire hazards;

• Suitable for high and low-voltage power supply lines, especially fire retardant engineering of cables laid under environmental conditions such as channel, tunnel, and overhead in power plants, substations, iron and steel, chemical industry, construction, subways, mines, and ships;

• Applicable to all forms of fire spreading, effectively isolating fire spreading.

PRODUCT Technical indicators

SPECIFICATIONS： X-FHD-108
PROPERTY	VALUE	UNIT	TEST METHOD
Physical property
Tensile strength	≥3	MPa	GB/T 528-2009
Elongation at break	≥500	MPa	GB/T 528-2009
Tensile strength change rate	≤±20%	---	GB/T2951.12-2008
Change rate of elongation at break	≤±20%	---	GB/T 2951.12-2008
Water resistance	Immersion for 15 days, no bubbles, wrinkling delamination, cracking, and other phenomena	—	Ga478-2004
Acid resistance, alkali resistance, Salt tolerance	Immersion for 7 days, no bubbles, wrinkling, delamination,cracking, and other phenomena	—	Ga478-2004
Self viscosity	No loosening for 24 hours	—	Ga478-2004
Oxygen index	≥32	%	GB/T 2046.2-2009
Flame retardant grade	V-0	—	UL94-2015
Halogen content	The contents of bromine and chlorine are less than those of 900 ppm, respectively. The total content of bromine + chlorine is less than 1500ppm	—	EN14582:2016
Smoke density grade	≤15	—	GB/T 8627-2007
Data in the table represent average test results and are not to be used for specification purposes. The product user should make his l her own tests to determine the product.it's suitable for the intended use.